Plasma etching of diamond surfaces

ABSTRACT

The present invention relates to a method of producing a diamond surface including the steps of providing an original diamond surface, subjecting the original diamond surface to plasma etching to remove at least 2 nm of material from the original surface and produce a plasma etched surface, the roughness R q  of the plasma etched surface at the location of the etched surface where the greatest depth of material has been removed satisfying at least one of the following conditions: R q  of the plasma etched surface is less than 1.5 times the roughness of R q  of the original surface, or R q  of the plasma etched surface is less than 1 nm.

BACKGROUND TO THE INVENTION

Diamond is a difficult material to form into complex structures because of its hardness and chemical inertness. Traditionally diamond has been shaped by lapidary techniques such as lapping and polishing using fine diamond grits and powders as the abrasive medium. One typical product of such processes is faceted natural diamonds used as jewellery. Examples of industrial products formed by lapidary processes are polycrystalline diamond plates used as exit windows for high power CO₂ lasers. In all these cases, the finished diamond product has large flat surfaces (i.e. extending laterally greater than a few 10 s of micrometers), ostensibly free from surface features which affect the performance.

The use of lapidary processes on diamond has the disadvantage that they result in the surface being processed having a ‘damaged zone’ that extends to a depth roughly equal to the diamond particle size used for processing.

For applications that require fine three-dimensional surface structural features, lapidary methods are not suitable. Liquid chemical etching processes, such as are used extensively in the microelectronics industry are not applicable to diamond because diamond is resistant to almost all chemicals.

High temperature gas phase etching processes have been used to etch diamond. The use of hydrogen-argon-oxygen and hydrogen-argon plasmas at high temperature (>700° C.) to etch substrates prior chemical vapour deposition (CVD) diamond synthesis is disclosed in WO 01/96633. Such an etch preferentially etches damage features associated with the sub-surface damage layer and therefore the roughness R_(q) is generally significantly increased as a result of the etch process.

In typical reactive ion etching (RIE) processes, large numbers of ions are produced that are accelerated towards the target and physically remove material by sputtering and related processes. The process can have low selectivity between materials and therefore is not always ideal for patterning surfaces. EP1555337 discloses the use of a reactive ion etch (RIE) using an oxygen-carbon fluoride (O₂—CF₄) gas mixture at a pressure of 1.33-13.3 Pa (about 10-100 mTorr) to prepare mechanically processed single crystal diamond surfaces for CVD growth.

In contrast to RIE, inductively-coupled plasma (ICP) etching is a largely chemical process in which a plasma is used to breakdown the etching gases into a mixture of free radicals (i.e. neutral species) and ions (i.e. charged species). The plasma is remote from the substrate being etched. Between the plasma and the diamond being etched, the vast majority of the ions generated in the plasma are removed. Thus the majority of species that reach the diamond are neutral. The resulting etching is therefore largely chemical (e.g. surface reactions leading to volatile products), rather than physical (e.g. sputtering from the surface by ions from the plasma). Since atoms in a higher energy state in the substrate, such as those in a region with extended lattice imperfections (e.g. a damaged region), are easier to etch, then this type of etch generally preferentially etches the regions of extended lattice imperfections, roughening the surface.

The use of inductively-coupled plasma (ICP) etching with an argon-oxygen gas mixture to pattern natural single crystal diamond is reported in H. W. Choi et al, ‘Properties of natural diamond microlenses fabricated by plasma etching’, Industrial Diamond Review, Issue 2, 2005, page 29, and to pattern polycrystalline diamond made by a chemical vapour deposition process in M. Karlsson et al, ‘Transfer of continuous-relief diffractive structure into diamond by use of inductively coupled plasma dry etching’, Optics Letters, 26 (2001), 1752-1754. UK Patent Application GB 2 281 254 discloses the use of a mixture of oxygen and fluorine containing gases in a plasma etching method for diamond. No disclosure is made about the roughness of the etched surfaces.

ICP etching of gallium nitride (GaN) using an Ar/Cl₂ gas mixture is reported in H. W. Choi et al, Journal of Applied Physics, 97 (2005), 063101.

SUMMARY OF THE INVENTION

The invention is a method of producing a diamond surface by plasma etching from an original surface which may be prepared by a traditional lapidary process, lapping or polishing or just polishing or from an as-grown surface. The invention also extends to a diamond surface, or portion of a diamond surface, which has been produced using the method of the invention.

According to a first aspect to the present Invention there is provided a method of producing a diamond surface including the steps of providing an original diamond surface, subjecting the original diamond surface to plasma etching to remove at least 2 nm of material from the original surface and produce a plasma etched surface, the roughness Rq of the plasma etched surface at the location of the etched surface where the greatest depth of material has been removed satisfying at least one of the following conditions:

-   a. Rq of the plasma etched surface Is less than 1.5 times the     roughness of Rq of the original surface, or -   b. Rq of the plasma etched surface is less than 1 nm.

Preferably both conditions are satisfied.

In a second aspect, the present invention provides a method of producing a diamond surface including the steps of providing an original diamond surface which has been mechanically processed; and subjecting the original diamond surface to plasma etching to remove at least 2 nm of material from the original surface and produce a plasma etched surface, wherein the plasma etched surface is substantially free from residual damage due to mechanical processing.

In the first and second aspects of the invention, preferably the diamond is CVD diamond, most preferably single crystal CVD diamond.

Preferably at least one structural feature is etched into either part of or all of the surface.

Preferably the plasma etching utilises an isotropic etch, preferably an Inductively-coupled plasma. The gas mixture used In the plasma etching may contain an inert gas and a halogen containing gas. Preferably the inert gas is argon.

The halogen containing gas may contain chlorine in which case preferably the halogen containing gas is molecular chlorine (Cl₂).

Preferably, in a method according to the present invention:

the maximum depth of the etched structural feature in a direction perpendicular to the original surface of the diamond is preferably less than 20 μm, and,

the smallest lateral dimension of the structural feature is preferably at least 0.5 times the maximum depth of the feature.

According to a third aspect of the present invention there is provided a method of producing an etched diamond surface including the steps of providing a diamond surface and subjecting the diamond surface to inductively coupled plasma etching using a gas mixture containing an inert gas and a halogen containing gas.

Preferably the diamond is CVD diamond, most preferably single crystal CVD diamond.

Alternatively the diamond may be polycrystalline CVD diamond.

According to a fourth aspect to the present invention there is provided a single crystal diamond having an etched surface or part of an etched surface resulting from at least 2 nm having been removed from a surface or a part of a surface of the diamond by etching, the etched surface having an Rq of less than 1 nm.

Preferably the diamond is CVD diamond.

The etching method Is preferably a method according to the first, second and third aspects to the present invention as hereinbefore described.

According to a fifth aspect to the present Invention there Is provided a polycrystalline CVD diamond comprising an etched surface or part of an etched surface resulting from at least 0.5 μm having been removed from a surface or a part of a surface of the diamond by etching, the etched surface having a surface roughness Rq of less than 5 nm.

The etching method is preferably a method according to the first, second and third aspects to the present invention as hereinbefore described.

The polycrystalline CVD diamond may be for use in an optical device.

The plasma etching process removes at least about 2 nm, preferably at least about 5 nm, preferably at least about 10 nm, preferably at least about 20 nm, preferably at least about 50 nm, preferably at least about 100 nm, preferably at least about 200 nm, preferably at least about 500 nm, preferably at least about 1000 nm, from the original surface or part of the original surface.

The plasma etching process preferably removes between about 2 nm and about 50 μm, more preferably between about 2 nm and about 20 μm, still more preferably between about 2 nm and about 10 μm, and still more preferably between about 2 nm and about 5 μm from the original surface.

The plasma etched surface of the invention has a roughness R_(q) ^(A) (After the etch) and the original surface a roughness R_(q) ^(B) (Before the etch), such that R_(q) ^(A)/R_(q) ^(B) is preferably less than about 1.5, more preferably less than about 1.4, more preferably less than about 1.2, more preferably less than about 1.1. Typically R_(q) ^(B) is prepared to an R_(q) of less than about 10 nm, more typically less than about 3 nm, more typically less than about 1 nm, more typically less than about 0.5 nm prior to the etch.

The R_(q) ^(B) and R_(q) ^(A) measurements are taken on the same area of the diamond. By “same area” Is meant an equivalent area as close as reasonably practical, using multiple measurements and statistical analysis where necessary to verify the general validity of the measurements, as is known in the art.

The particularly unusual advantage of this plasma etch is that it can improve the R_(q) of the diamond surface, particularly when applied to surfaces where the initial surface R_(q) ^(B) is prepared to an R_(q) of less than about 1 nm, more typically less than about 0.5 nm, more typically less than about 0.3 nm, thus providing a route to extremely low surface roughness values. Under these circumstances, the plasma etched surface of the invention has a roughness R_(q) ^(A), and the original surface before the etch a roughness, R_(q) ^(B), such that R_(q) ^(A)/R_(q) ^(B) is less preferably less than about 1.0, more preferably less than about 0.8, more preferably less than about 0.6, more preferably less than about 0.5, more preferably less than about 0.4, more preferably less than about 0.3.

The method thus provides a plasma etched diamond surface with an R_(q) value preferably less than about 1 nm, preferably less than about 0.5 nm, preferably less than about 0.3 nm, preferably less than about 0.2 nm, preferably less than about 0.1 nm. Furthermore this plasma etched diamond surface with low R_(q) preferably is largely free of processing damage such that the number of defects revealed by the revealing etch test is less than about 100 per mm².

For the purposes of this invention the roughness of a surface is described by its R_(q) value. R_(q) is also known as the ‘root mean square’ (or RMS) roughness. R_(q) is defined as the square root of the mean squared deviations from the centre-line or plane of the surface profile:

R _(q)=√((y ₁ ² +y ₂ ² + . . . +y _(n) ²)/n)

where y₁ ² etc are the squared deviations from the centre-line or plane of the surface profile and n is the number of measurements.

A surface may also be quantified by its R_(a) value (also referred as ‘average roughness’ or ‘centre line average’):

R _(a)=(|y ₁ |+|y ₂|+ . . . |y_(n)|)/n

where |y₁| etc are the moduli of the deviations from the centre-line or plane of the surface profile and n is the number of measurements.

For a surface with a Gaussian distribution of deviations from the centre-line or plane of the surface profile, the value of R_(q)=1.25×R_(a).

R_(a) and R_(q) may be measured along lines (a one-dimensional measurement) or over areas (a two-dimensional measurement). An area measurement is essentially a series of parallel line measurements.

For the purposes of this invention the R_(q) value is normally measured over an about 1 μm by about 1 μm area or about 2 μm by about 2 μm area using a scanning probe instrument such as an atomic force microscope (AFM). In certain circumstances, It is considered more appropriate to measure the R_(q) using a stylus profilometer over a 0.08 mm scan length.

The phrase ‘structural feature’ or ‘topographic feature’ is used throughout this specification to refer to desirable features or structure etched into the diamond In a controlled fashion, to provide useful function. In particular this is distinct from features arising in the surface of the diamond from anisotropic etching of sub-surface damage, which are referred to as ‘damage features’

There are a number of application areas for this invention, each using a particular combination of the benefits given by this invention:

-   -   i) The preparation of structural features suitable for use in         electronic structures such as transistor gate trenches etc. Such         structural features in electronic structures are preferably in         the range of about 2 nm to about 100 nm in depth, more         preferably in the range about 2 nm to about 30 nm in depth. The         method of this invention can provide low and controlled etch         rates, with etch rates preferably less than about 0.08 μm/min,         more preferably less than about 0.06 μm/min, more preferably         less than about 0.04 μm/min, which etch rate varies in a         relatively linear fashion with ICP coil power. Furthermore, the         incubation time, or delay time at the start of the etch between         applying the external process conditions and obtaining etching         is small, typically less than about 5 seconds, more typically         less than about 3 seconds, and consistent, so that precise etch         depth control can be achieved. The isotropic nature of the etch         of this invention gives surfaces where the presence of any         damage features after the etch do not significantly roughen the         surface, or more preferably where the etched surface is even         smoother than the initially prepared surface, as described         above.     -   ii) The preparation of structural features in the surface of the         diamond for use in optical applications such as microlenses, and         other applications needing relatively large topographic         features, particularly with smooth curved surfaces. Such         topographic features are preferably in the range of about 200 nm         to about 20 μm in depth or vertical height of the features         formed, more preferably in the range about 500 nm to about 5 μm         in depth or vertical height of the features formed. The method         of this invention can provide controlled etch rates, with etch         rates preferably greater than about 0.08 μm/min, more preferably         greater than about 0.10 μm/min, which etch rate varies in a         relatively linear fashion with ICP coil power. Furthermore, the         incubation time, or delay time at the start of the etch between         applying the external process conditions and obtaining etching         is small, typically less than about 5 seconds, more typically         less than about 3 seconds, and consistent, so that precise etch         depth control can be achieved. A particular benefit of this         method is the low etch selectivity, made use of by applying a         variable thickness of mask and enabling the etch to break         through the mask to the diamond in at least some regions. The         low etch selectivity enables relatively thick layers of mask to         be used, reducing tolerances and difficulty in applying this         layer, for the same final structural features in the diamond.         The etch selectivity in applications of this type is preferably         less than about 0.16, more preferably less than about 0.14, more         preferably less than about 0.12, more preferably less than about         0.10, more preferably less than about 0.09. The etch selectivity         is defined as:

(etch rate of mask)/(etch rate of diamond)

-   -   -   The isotropic nature of the etch of this invention gives             surfaces where the presence of any damage features after the             etch do not significantly roughen the surface, or more             preferably where the etched surface is even smoother than             the initially prepared surface, as described above.

    -   iii) The preparation of surfaces or surface regions for further         epitaxial growth, preferably for further growth of CVD diamond,         or for preparing surfaces free of damage for electrical contacts         on, for example, Schottky diodes, three-terminal electronic         devices (such as field effect transistors) radiation detectors,         sensors etc. Such preparation requires the removal of sufficient         depth to significantly reduce the surface damage and thus needs         to be of the same order of thickness as the surface damage         layer. Typically surface damage layers have thicknesses in the         range of about 0.2 μm to about 20 μm (or thicker with very         aggressive lapidary techniques). Thus preferably the etch         removes a thickness of material from the surface, where the         thickness of material removed is at least about 0.2 μm, more         preferably at least about 0.5 μm, more preferably at least about         1.0 μm, more preferably at least about 2 μm, more preferably at         least about 5 μm, more preferably at least about 10 μm. The         surface damage layer typically has a thickness that is about the         same as the size of the largest diamond grit particle used for         the last stage of lapidary processing; for example a surface         scaife polished with 1-2 μm sized diamond grit will typically         have a surface damage layer about 2 μm thick. Therefore, to         minimise the amount of damage from lapidary processing that         remains after etching by the method of the invention, the amount         of material removed by the method of the invention should         preferably be at least about 0.2 times the size of the largest         grit particles, more preferably at least about 0.5 times the         size of the largest grit particles, more preferably at least         about 0.8 times the size of the largest grit particles, more         preferably at least about 1.0 times the size of the largest grit         particles, more preferably at least about 1.5 times the size of         the largest grit particles, more preferably at least about 2         times the size of the largest grit particles. There is benefit         in the surface roughness after such an etch remaining low, to         avoid defects in the overgrown layer arising from damage         features etched into the diamond surface. In particular, where         the surface is single crystal diamond the surface preferably has         a surface roughness after the etch, R_(q), of less than about 10         nm, more preferably less than about 5 nm, more preferably less         than about 2 nm, more preferably less than about 1 nm, more         preferably less than about 0.5 nm, more preferably less than         about 0.3 nm. Alternatively, where the surface is         polycrystalline CVD diamond the surface preferably has a surface         roughness after the etch, R_(q), of less than about 40 nm, more         preferably less than about 20 nm, more preferably less than         about 10 nm, more preferably less than about 5 nm, more         preferably less than about 2 nm, more preferably less than about         1 nm. The method of this Invention can provide controlled etch         rates, with etch rates preferably greater than about 0.08         μm/min, more preferably greater than about 0.10 μm/min, which         etch rate varies in a relatively linear fashion with ICP coil         power. Furthermore, the incubation time, or delay time at the         start of the etch between applying the external process         conditions and obtaining etching is small, typically less than         about 5 s, more typically less than about 3 s, and consistent,         so that precise etch depth control can be achieved. The         isotropic nature of the etch of this invention gives surfaces         where the presence of any damage features after the etch do not         significantly roughen the surface, or more preferably where the         etched surface is even smoother than the initially prepared         surface, as described above.

The maximum depth of an etched structural feature in a direction perpendicular to the major surface of the diamond is preferably less than about 20 microns, more preferably less than about 10 microns, more preferably less than about 5 microns, more preferably less than about 2 microns, more preferably less than about 1 micron, more preferably less than about 500 nm, more preferably less than about 200 nm, more preferably less than about 100 nm, more preferably less than about 60 nm, and the smallest lateral dimension of the etched structural feature is preferably at least about 0.5 times the maximum depth, more preferably at least about 1 times the maximum depth, more preferably at least about 2 times the maximum depth, more preferably at least about 5 times the maximum depth, more preferably at least about 10 times the maximum depth, more preferably at least about 15 times the maximum depth.

In an embodiment, the present invention provides a method of producing a diamond surface including the steps of providing an original diamond surface, subjecting the original diamond surface to plasma etching, preferably isotropic plasma etching, more preferably inductively-coupled plasma etching to remove at least 2 nm of material from the original surface and produce a plasma etched surface, the roughness R_(q) of the plasma etched surface at the location of the etched surface where the greatest depth of material has been removed satisfying at least one of the following conditions:

-   -   a. R_(q) of the plasma etched surface is less than 1.5 times the         roughness of R_(q) of the original surface, or     -   b. R_(q) of the plasma etched surface is less than 1 nm; and         wherein, preferably the gas mixture used in the plasma etching         contains an inert gas, preferably argon and a halogen containing         gas, preferably chlorine.

The invention provides, according to another aspect, a single crystal diamond having an etched surface or part of an etched surface resulting from at least about 2 nm having been removed from a surface or a part of a surface of the diamond by etching, the etched surface having an R_(q) of less than about 1 nm.

The invention provides according to yet another aspect, a polycrystalline CVD diamond comprising an etched surface or part of an etched surface resulting from at least about 0.5 μm having been removed from a surface or a part of a surface of the diamond by etching, the etched surface having a surface roughness R_(q) of less than about 5 nm.

In an embodiment, the invention provides a single crystal diamond having an etched surface or part of an etched surface resulting from at least about 2 nm having been removed from a surface or a part of a surface of the diamond by etching, the etched surface having an R_(q) of less than about 1 nm, preferably less than about 0.5 nm, preferably less than about 0.3 nm, preferably less than about 0.2 nm, preferably less than about 0.1 nm.

In another embodiment, the invention provides a polycrystalline CVD diamond comprising an etched surface or part of an etched surface resulting from at least about 0.5 μm having been removed from a surface or a part of a surface of the diamond by etching, the etched surface having a surface roughness R_(q) of less than about 5 nm, preferably less than about 2 nm, preferably less than about 1 nm, preferably less than about 0.5 nm, preferably less than about 0.3 nm, preferably less than about 0.2 nm, preferably less than about 0.1 nm.

The plasma etched surface can either be in the form of the whole extent of a diamond surface or a proportion of the surface such as structural features etched Into the surface as part of the process for making electronic devices, optical elements such as micro-lenses, micro-electro-mechanical systems (MEMS), X-ray optical elements etc.

The method of the invention results in a surface or surface structural features that, after undergoing the plasma etching process, are essentially free of the damage characteristic of diamond surfaces prepared by the traditional processes such as lapidary processes of either lapping and polishing or just polishing.

The extent of sub-surface damage can be revealed and quantified using a deliberately anisotropic thermal revealing etch. The revealing etch preferentially oxidises regions of damaged diamond and therefore allows such regions to be identified and thereafter quantified. Regions containing sub-surface damage from mechanical processing are typically darkened or even blackened by the revealing etch.

The revealing etch consists of:

-   -   (i) examining the surface at a magnification of 50 times using         reflected light with a typical metallurgical microscope to         ensure that there are no surface features present,     -   (ii) exposing the surface to an air-butane flame thereby raising         the diamond surface to a temperature of typically about 800° C.         to about 1000° C. for a period of about 10 seconds,     -   (iii) examining the surface at a magnification of 50 times using         reflected light with a typical metallurgical microscope and         counting the damage features revealed by the revealing etch, in         the manner described below, to determine their number density,     -   (iv) repeating steps (ii) and (iii) and comparing the measured         density of defects with that of the previous cycle until the         following condition is met: if the number density of defects         counted is less than or equal to about 150%, preferably less         than or equal to about 120%, of the number density determined in         the previous cycle, then all the defects are deemed to be         revealed and the measurement recorded is the average of the         measurements of the last two cycles, if not the cycle is         repeated again.

The number density of defects is measured by the following method:

-   -   (i) the defects to be counted are those defects visible at a         magnification of 50 times with a typical metallurgical         microscope which fall totally or partially within a rectangular         area 1 mm×0.2 mm projected onto the surface being characterised,     -   (ii) the area is selected at random over the surface or portion         of the surface to be characterised and randomly oriented,     -   (iii) the defects are counted in a minimum of 5 such areas,     -   (iv) the number density of defects is calculated by dividing the         total number of defects counted by the total area examined to         give a number density in defect per mm².

To measure the number density of defects in areas less than about 1 mm² the above method is adapted by completing the defect count over the whole area as a single measurement.

For the surface to be considered to be substantially free of residual damage due to mechanical processing the number density of defects revealed in a surface of single crystal CVD diamond prepared by the method of the invention is less about 100 mm², preferably less than about 50 per mm², preferably less than about 20 per mm², preferably less than about 10 per mm², preferably less than about 5 per mm².

Alternatively, the technique of “Rutherford backscattering” (or “RBS”) may be used to at least semi-quantitatively evaluate the extent of sub-surface damage in a sample. The technique of RBS is well known in the art (for example see the article “Ion Backscattering Analysis” in “Concise Encyclopedia of Materials Characterization”, Eds R. W. Cahn and E. Lifshin, Pergamon (London), 1993, pages 199-204). RBS is an ion beam technique that that can probe up to about 1 μm beneath the surface of a crystalline solid. Information about the crystallographic perfection of the near surface layer can be obtained by the use of “channelling”, wherein the higher the crystallographic perfection of the surface layer, the lower the backscatter ion yield, such that for a perfect surface, there is substantially no backscattered Ion yield (where substantially means less than about 5%, preferably less than about 3%, preferably less than about 2%, preferably less than about 1%, of the incident ions are backscattered).

The surface of the invention is produced by plasma etching, preferably using an inductively-coupled plasma (ICP) etching process, and preferably at an operating pressure in the range of about 0.5 mTorr (about 0.0667 Pa) to about 100 mTorr (about 13.3 Pa), more preferably in the range of about 1 mTorr (about 0.133 Pa) to about 30 mTorr (about 4.00 Pa), more preferably in the range about 2 mTorr (about 0.267 Pa) to about 10 mTorr (1.33 Pa). The etchant is preferably a gas mixture consisting of at least an inert gas, preferably argon, and a halogen-containing gas, preferably chlorine (Cl₂). Preferably the halogen containing gas is present in the gas mixture added to the process in a concentration (by volume) in the range about 1%—about 99%, more preferably about 20%—about 85%, more preferably about 40%—about 70%. Preferably the majority of the balance of the gas mixture is made up with Ar, more preferably the whole of the balance of the gas is made up with Ar.

Alternatively the inert gas may be helium, neon, krypton or xenon, or may comprise a mixture of more than one of these, or may comprise a mixture of one or more of these with argon.

The plasma etching process of the invention is essentially a chemical process, therefore it etches diamond surfaces of all orientations at approximately the same rate, that is, the process can be described as being ‘isotropic’. Therefore the process can be used to etch polycrystalline CVD diamond, a polished surface of which typically contains grains in a variety of orientations relative to the surface.

The method of the invention is compatible with conventional lithographic processes that might be used for the fabrication of electronic devices. For example it might be used to produce structural features on the surface of a diamond by applying a suitable resist to the surface, appropriately patterning the resist and then etching the surface using the same ICP process as previously described.

The method of the invention can be applied to surfaces comprising natural single crystal diamond, synthetic single crystal diamond made by high pressure-high temperature (HPHT) techniques, synthetic single crystal diamond made by CVD techniques (‘single crystal CVD diamond’), and synthetic polycrystalline diamond made by CVD techniques (‘polycrystalline CVD diamond’).

The method of the present invention gives the following advantages over the prior art:

-   -   the method can be used to pattern a surface with structural         features, the patterning being done using standard         lithographical methods,     -   the method can be used to etch both single crystal and         polycrystalline diamond without revealing pits due to         dislocations in the former and grain boundaries in the latter,     -   the method can be used to etch damaged surfaces without         preferentially removing the damaged regions and hence without         significantly roughening the surfaces,     -   the method can be used to remove damage and hence prepare         damage-free surfaces for epitaxial growth,     -   the method can be used to remove damage and hence prepare         damage-free surfaces for electrical contact formation,     -   the method can be used on the surfaces of optical components,     -   the roughness of the surface is not significantly increased by         undertaking the etching process,     -   the diamond surfaces obtained after removing sufficient material         by etching can be essentially free of damage associated with         mechanical surface processing.

The plasma etched diamond surface of the present invention can be used for a wide range of applications, including, for example, preparation of substrates for electronic device manufacture free of a damage layer, preparation of substrates for synthesis of homoepitaxial diamond layers by chemical vapour deposition, fabrication of three-dimensional structural features and surface preparation to enable high performance electrical contacts to be made to the surface.

It is surprising that diamond can be etched using an Ar-Hal, particularly an Ar—Cl₂, gas mixture. Diamond is a highly unreactive solid. Halogens are known to stabilise the surface of diamond during CVD growth processes which occur at temperatures between 500° C. and 1200° C. Inert gases are often used as charged species in PVD etching process, but in ICP the component of etching attributed to charged species is negligible.

As used herein, the term “about x” is intended to include the value x itself.

Thus, the invention provides according to yet another aspect a method of producing an etched diamond surface including the steps of providing a diamond surface and subjecting the diamond surface to Inductively coupled plasma etching using a gas mixture containing an inert gas, preferably argon and a halogen containing gas, preferably chlorine.

BRIEF DESCRIPTION OF THE FIGURES

The following figures are referred to in examples 1 to 6.

FIG. 1 is a scanning electron micrograph of an Ar/Cl ICP plasma etched trench approximately 16 nm deep.

FIG. 2 is an atomic force microscopy image of a region of the trench in FIG. 1.

FIG. 3 is a scanning electron micrograph of an Ar/Cl ICP plasma etched trench approximately 53 nm deep.

FIG. 4 is an atomic force microscopy image of a region of the trench in FIG. 3.

FIG. 5 is line drawing based on an atomic force microscopy image of an Ar/Cl ICP plasma etched diamond micro-lens

FIG. 6 is a measured line profile across the centre of the diamond micro-lens shown in FIG. 5, along with a fitted profile with ideal spherical curvature.

FIG. 7 is a plot of etch rate and etch selectivity against ICP coil power.

FIG. 8 is a plot of etch rate versus etch time.

FIG. 9 is an atomic force microscopy image of a HPHT diamond surface polished using a resin-bonded wheel.

FIG. 10 is an atomic force microscopy image of the HPHT diamond sample in FIG. 9 following Ar/Cl ICP plasma etching.

DETAILED DESCRIPTION OF THE EMBODIMENTS

The details of the invention will be described using six examples. The first example describes the use of the invention for making an essentially damage free surface on a series of single crystal CVD diamond plates and comparing the resultant surfaces with a sample that has not been etched. The second example describes the use of the invention for making fine structural features on a polycrystalline CVD diamond plate.

Example 1

Four single crystal CVD diamond plates approximately 4 mm×4 mm×0.5 mm were laser sawn from larger as-grown blocks of single crystal CVD diamond made by the method disclosed in WO 01/96633. The large planar surfaces of the plates (hereinafter referred to as the ‘major surfaces’) were oriented within a few degrees of {100} crystallographic surfaces. The smaller surfaces forming the edges of the plates (hereinafter referred to as the ‘edge surfaces’) were approximately parallel to <100> directions.

The major surfaces of all four plates were initially lapped on a cast iron lapping wheel using progressively finer diamond grit suspended in a cellulose-based carrier. The final lapping stage used diamond grit in the size range 15 μm to 25 μm and the roughness R_(q) measured using a stylus profilometer over a 0.8 mm length was in the range 100 to 150 nm for all three plates. Previous experiments have indicated that after this stage of lapping, the sub-surface damaged layer extends to a depth of approximately 10 μm beneath the surface.

All of the plates were chosen at random and their major surfaces were polished using a traditional diamond polishing scaife. Two cast iron scaife-wheels were used, the first prepared with diamond powder in the size range 2-4 μm and the second with diamond powder in the size range 1-2 μm. The depth of material removed during the scaife polishing process was determined to be approximately 15 μm. After completion of the scaife processing, the R_(q) values measured using a stylus profilometer over an 80 μm length were less than 5 nm. More accurate measurements over areas (e.g. about 1 μm by about 1 μm) made with an atomic force microscope gave the R_(q) values listed in Table 1.

One of the plates (referred to as ‘Sample 1’) was selected at random and subjected to the thermal revealing etch according to the method previously described (heating the surface in air to about 850° C. for 10 seconds using a small air-butane blow torch). The defects were counted according to the method of the invention. The plate showed considerable evidence of sub-surface damage, very much greater than 100 defects per mm².

The other three plates (referred to as ‘Sample 2’, ‘Sample 3’ and ‘Sample 4’) were subjected to inductively coupled plasma etches to remove material from the surface. The ICP etching conditions were: a platen power of approximately 300 W, a coil power of approximately 400 W, a chamber pressure of 5 mTorr (0.667 Pa), flow rates of 25 sccm for Ar and 40 sccm for Cl₂. The etching times chosen for the three samples were 15, 30 and 60 minutes. The amount of material removed from the etched surfaces, the initial and final surface roughness, R_(q), values are in Table 1.

TABLE 1 Characteristics of plates before and after plasma etching R_(q) after scaife Plasma etching R_(q) after plasma Approximate depth of Sample polishing, nm time, minutes etching, nm material removed, nm 1 0.9 N/A N/A N/A 2 1.2 15 1.1  900 3 0.9 30 0.7 2000 4 0.7 60 0.5 4000

After the plasma etching process and after the measurement of the R_(q), all three plates were subjected to the thermal revealing etch to evaluate the extent of sub-surface damage. For each of samples 2 to 4 the number density of defects measured was in each case less than 10, unlike that revealed in sample 1, which was the plate not subjected to the plasma etch.

Example 2

Two samples of polycrystalline CVD diamond about 10 mm×10 mm in lateral extent and about 650 μm thick were polished on their growth surfaces using conventional lapidary processes. The surface roughness values, R_(q), of the polished plates, measured by atomic force microscopy over a 2 μm by 2 μm area were 1.0 nm and 1.0 nm.

Micro-trenches were etched into the two samples of polycrystalline diamond using an Ar—Cl₂ ICP plasma. Micro-trench photoresist features were mask patterned on the surface of the samples using standard lithographic methods. The samples were etched using the following ICP chamber conditions: a platen power of approximately 300 W, a coil power of approximately 400 W, a chamber pressure of 5 mTorr (0.667 Pa), flow rates of 25 sccm for Ar and 40 sccm for Cl₂. In the first sample trenches of depth 16 nm were etched [FIG. 1 and FIG. 2] and in the second sample trenches of depth 53 nm were etched [FIG. 3 and FIG. 4]. It can be seen that the trench walls are well-defined, with no rough edges apparent. The etch rates were measured to be approximately 1 nm per second in both cases, which demonstrates the reproducibility of this method. It is also clear that the surfaces post-etch show no indication of the grain boundaries in these polycrystalline samples, which demonstrates that the etch Is isotropic in nature. The R_(q), values (measured over 1 μm×1 μm areas using an atomic force microscope) of the samples after etching the 16 and 53 nm deep trenches are 0.8 and 1.1 nm respectively, which should be compared to the pre-etched surface roughness of 1.0 nm. This indicates that under these conditions little or no surface roughening is caused using this etching method, and further supports the conclusion that the etch is isotropic.

Example 3

Spherical micro-lens structures were fabricated in a sample of single crystal IIa natural diamond using Ar/Cl₂ ICP etching in conjunction with the photoresist reflow method [H. W. Choi, E. Gu, C. Liu, J. M. Girkin, M. D. Dawson, J. of Appl. Phys. 97 (6), 063101 (2005); C. L. Lee, H. W. Choi, E. Gu, M. D. Dawson, Dia. Rel. Mat. 15, 725 (2006)]. A 7 μm thick layer of Shipley SPR220 photoresist was spin-coated onto the diamond substrate first. After mask patterning, the photoresist pillars were formed. The sample was then placed on a hotplate at 125° C. for 2 minutes to allow the photoresist pillars to re-flow. Due to the surface tension, spherical lens structures were formed. These lens structures were then transferred onto the diamond substrate by ICP etching using Ar/Cl₂ plasma. The ICP parameters used were: a platen power of 100 W, a coil power of 400 W, a chamber pressure of 5 mTorr (0.667 Pa), flow rates of 25 sccm for Ar and 40 sccm for Cl₂, with an etching duration of 25 minutes.

A line drawing based on an atomic force microscopy image of a representative diamond micro-lens is shown in FIG. 5. The surface diameter and height of the lens were measured to be 50 μm and 0.75 μm respectively. The profile of the diamond micro-lenses was studied by examining the cross-sectional scan of the atomic force microscopy images. The measured profile was then compared to the curvature of a circle. The measured cross-sectional profile of the diamond micro-lens and the fitted spherical profile are plotted in FIG. 6. It can be seen that the deviation from the ideal profile Is very small, indicating the cross-sectional profile of the micro-lens is very close to spherical in shape.

Example 4

The etch rate and etch selectivity (as defined earlier) of the Ar/Cl₂ ICP plasma was investigated as a function of the ICP coil power using the following conditions: ICP coil powers of 100 W. 400 W and 900 W; a constant ICP platen power of 300 W; a chamber pressure of 5 mTorr (0.667 Pa); flow rates of 25 sccm for Ar and 40 sccm for Cl₂; an etching duration of 5 minutes. Single crystal natural diamond samples were used for these experiments and photoresist was used as the mask material. The results are plotted In FIG. 7. It is observed that the etch rate increases linearly with the ICP coil power and etch selectivity is approximately constant (at around 0.09). In a similar experiment the etch selectivity on type Ib synthetic single crystal diamond was also found to be around 0.09. This should be compared to the etch selectivity using an Ar/O₂ ICP plasma, which is around 0.20 [C. L. Lee, H. W. Choi, E. Gu, M. D. Dawson, Dia. Rel. Mat. 15, 725 (2006)]. Hence, using photoresist masks of identical thickness, the height or depth of microstructures fabricated in diamond (such as micro-lenses and micro-trenches) using ICP Ar/Cl₂ etching would be approximately half of those fabricated using ICP Ar/O₂ etching. Thus the lower etch selectivity obtained using Ar/Cl₂ is more suitable for etching shallower structural features into diamond in which precise control on the depth or height of the microstructure is required.

Example 5

Etch rate as a function of time was investigated by etching micro-trenches in type Ib synthetic single crystal diamond samples. Trenches were etched in three samples using identical photoresist masks and under Ar/Cl₂ ICP plasma conditions identical to those described In Example 2. The three samples were etched respectively for 9, 20 and 40 seconds. The depths of the micro-trenches formed were measured by atomic force microscopy and are plotted In FIG. 8 as a function of the etch time. The mean etch rate was extracted by performing a simple linear curve fit to the data, and found to be 1.29±0.03 nm s⁻¹. The small uncertainty in this number indicates that the method yields a reproducible etch rate, which is an important requirement of a manufacturing process.

Example 6

A type Ib HPHT single crystal sample, mechanically polished using a resin-bonded polishing wheel, was etched for 10 minutes using the following ICP chamber conditions: a platen power of approximately 300 W, a coil power of approximately 100 W, a chamber pressure of 5 mTorr (0.667 Pa), flow rates of 25 sccm for Ar and 40 sccm for Cl₂. FIG. 9 shows a representative atomic force microscope scan over a 1 μm×1 μm surface area of the polished sample prior to ICP etching. The surface is characterised by nanometre-scale linear trenches or grooves resulting from the polishing and the roughness R_(q) over this area was measured to be 0.53 nm. FIG. 10 shows a representative AFM scan over a 1 μm×1 μm surface area of the sample after the ICP etch. It can be seen that the linear polishing grooves are shallower than before and the roughness R_(q) over this area was measured to be 0.19 nm. This example demonstrates the ability of this method to reduce the roughness of mechanically pre-polished diamond surfaces. 

1. A method of producing an etched diamond surface including the steps of providing an original diamond surface, subjecting the original diamond surface to plasma etching to remove at least 2 nm of material from the original surface and produce a plasma etched surface, the roughness R_(q) of the plasma etched surface at the location of the etched surface where the greatest depth of material has been removed satisfying at least one of the following conditions: a. R_(q) of the plasma etched surface is less than 1.5 times the roughness of R_(q) of the original surface, or b. R_(q) of the plasma etched surface is less than 1 nm.
 2. A method according to claim 1 wherein both conditions are satisfied.
 3. A method according to claim 1, wherein the original diamond surface has been mechanically processed prior to being subjected to the plasma etching.
 4. A method of producing an etched diamond surface including the steps of providing an original diamond surface which has been mechanically processed; and subjecting the original diamond surface to plasma etching to remove at least 2 nm of material from the original surface and produce a plasma etched surface, wherein the plasma etched surface is substantially free from residual damage due to mechanical processing.
 5. A method according to claim 4, wherein the number density of defects revealed by an anisotropic thermal revealing etch in the plasma etched surface is less than about 100 per mm².
 6. A method according to claim 1 wherein at least one structural feature is etched into either a part of or all of the surface.
 7. A method according to claim 1, wherein the plasma etch is isotropic.
 8. A method according to claim 1 wherein the plasma etching utilises an inductively-coupled plasma, and a gas mixture used in the plasma etching contains an inert gas and a halogen containing gas.
 9. (canceled)
 10. (canceled)
 11. A method according to claim 8 wherein the inert gas is argon and the halogen containing gas contains chlorine.
 12. (canceled)
 13. A method according to claim 1 wherein: a maximum depth of the etched structural feature in a direction perpendicular to the original surface of the diamond is less than 20 μm, and, the smallest lateral dimension of the structural feature is at least 0.5 times the maximum depth of the feature.
 14. A method of producing an etched diamond surface including the steps of providing an original diamond surface and subjecting the original diamond surface to inductively coupled plasma etching using a gas mixture containing an inert gas and a halogen containing gas.
 15. A method according to claim 14 wherein the original diamond surface comprises CVD diamond.
 16. A method according to claim 15 wherein the diamond is single crystal CVD diamond.
 17. A method according to claim 15 wherein the diamond is polycrystalline CVD diamond.
 18. A single crystal diamond having an etched surface or part of an etched surface resulting from at least 2 nm having been removed from a surface or a part of a surface of the diamond by etching, the etched surface having an R_(q) of less than 1 nm.
 19. A single crystal diamond according to claim 18, wherein the number density of defects revealed by an anisotropic thermal revealing etch in the plasma etched surface is less than about 100 per mm².
 20. A single crystal diamond according to claim 18, wherein the etching method is a method according to claim
 1. 21. A polycrystalline CVD diamond comprising an etched surface or part of an etched surface resulting from at least 0.5 μm having been removed from a surface or a part of a surface of the diamond by etching, the etched surface having a surface roughness R_(q) of less than 5 nm.
 22. A polycrystalline CVD diamond according to claim 21, wherein the number density of defects revealed by an anisotropic thermal revealing etch in the plasma etched surface is less than about 100 per mm².
 23. A polycrystalline diamond according to claim 21 wherein the etching method is a method according to claim
 1. 24-27. (canceled) 